Control of thermal homogeneity of normalizing process for P92 steel

Thermal Power Generation Vol. 46, Issue 2, Pages: 100-104(2017)

更新时间：2025-09-28

- Control of thermal homogeneity of normalizing process for P92 steel
- 作者机构：
  
  1. 国网新源控股有限公司技术中心工程技术所
  2. 南瑞集团公司(国网电力科学研究院)
  3. 北京国电富通科技发展有限责任公司
- 作者简介：
- 基金信息：
- DOI：
  CLC： TG156.4
- Published：2017
- 稿件说明：
移动端阅览
ZHAO Qiang, AN Wei, SHENG Hui, et al. Control of thermal homogeneity of normalizing process for P92 steel[J]. Thermal Power Generation, 2017, 46(2): 100-104.
DOI：

ZHAO Qiang, AN Wei, SHENG Hui, et al. Control of thermal homogeneity of normalizing process for P92 steel[J]. Thermal Power Generation, 2017, 46(2): 100-104. DOI：

摘要

正火工艺对P92钢的性能影响较大

某台热处理炉对P92钢进行处理常出现金相不合格问题

对此

本文对该热处理炉的有效加热区进行了检定

同时通过控温精确的小加热炉模拟工业热处理炉低温加热区

并采用光学显微镜、扫描电子显微镜及透射电子显微镜对2种热处理后的P92钢试样进行组织观察。结果表明:正火过程中炉膛内温度存在偏差和炉膛底部温度明显偏低是造成P92钢金相不合格的主要原因;970℃正火与1 070℃正火后的P92钢性能基本无差异

金相组织均为细小的板条马氏体

属于合格金相组织;随着正火温度升高

微观组织的马氏体板条的宽度逐渐增加

强化相析出明显

持久强度提高

最小蠕变速率下降。

Abstract

Working zone of the industrial heat treatment furnace was checked

and the small-scale heating furnace with accurate temperature control was applied to simulate the low temperature heating zone of the industrial heat treatment furnace.Moreover

the optical microscope

scanning electron microscope and transmission electron microscope were used to observe the microstructure of the samples which have suffered different heat treatment processes.The results show that

the positive deviation of temperature in the furnace and the obvious low temperature at the bottom of furnace were the main reasons for metallographic " unqualified" for P92 steel.The mechanical properties of the samples after normalizing at 970℃and 1 070℃ nearly had no difference

the microstructure of both the samples were fine tempered martensite

which is qualified.With an increase in normalizing temperature

the width of martensite laths increased

the strengthening phases precipitated obviously

the persistent strength increased and the minimum creep rate decreased.

关键词

Keywords

references

Views

下载量

CSCD

Alert me when the article has been cited

提交

Publicity Resources

THE CARBIDE CONTAINED IN HCM25(T23) STEEL AND EVOLUTION REGULARITY THEREOF

STUDY ON SERVICING BEHAVIOR OF BOILER TUBES MADE FROM 18-8 TYPE AUSTENITIC STAINLESS STEEL(6)

TEST ASSESSMENT OF INDUCTIVE PIPEBENDING WITH BENDING RADIUS OF 1.5 D AND APPLICATION THEREOF

TEST STUDY ON THE INFLUENCE OF CARBONITRIDING UPON FLY ASH EROSION PERFORMANCE OF 20 CARBON STEEL

AN APPROACH TO THE CREEP PRPERTY OF P92 STEEL

Related Author

ZHANG Hongjun1 1.Xi'an Thermal Power Research Institute Co.Ltd.

TANG Liying1

ZHOU Rongcan1

HOU Shufang1

NIE Ming2

YU Zaisong1

SHI Zhigang

MA Hong

Related Institution

Guangdong Power Grid Corporation Electric Power Science Research Institute

Xi'an Thermal Power Research Institute Co., Ltd

Yangzi Petrochemical Shaoer Pipe Industry Co., Ltd

Nanjing University of Technology

Shanghai Electric Power University

AI问答

⁰