Thermal Power Generation Vol. 45, Issue 6, Pages: 111-115(2016)

更新时间：2025-09-28

- Failure analysis of flange used for urea hydrolysis equipment
- 作者机构：
  
  西安热工研究院有限公司
- 作者简介：
- 基金信息：
- DOI：
  CLC： TQ113.2;TG142.71
- Published：2016
- 稿件说明：
移动端阅览
HUANG Jinyang, YANG Zheng, LU Jintao, et al. Failure analysis of flange used for urea hydrolysis equipment[J]. Thermal Power Generation, 2016, 45(6): 111-115.
DOI：

HUANG Jinyang, YANG Zheng, LU Jintao, et al. Failure analysis of flange used for urea hydrolysis equipment[J]. Thermal Power Generation, 2016, 45(6): 111-115. DOI：

摘要

针对现役烟气脱硝用尿素水解装置中氨气出口密封法兰失效问题

采用宏观检验、金相分析、扫描电镜和X-射线衍射等方法

对TP304不锈钢材料密封法兰失效原因进行了分析。结果表明:法兰腐蚀失效主要是由尿素水解后高温高压中间产物引起的持续性点蚀和溶解腐蚀导致;腐蚀产物以Fe和Cr的氧化物为主

其结构疏松

存在大量孔洞和裂纹;TP304不锈钢不适宜用作烟气脱硝用尿素水解装置氨气出口密封法兰材料。

Abstract

By such tests as macroscopic inspection

metallographic analysis

scanning electron microscope(SEM)and X-ray diffraction(XRD)

the failure behavior of a seal flange made by TP304 stainless steel used at outlet of the urea hydrolysis equipment for flue gas denitrification was analyzed.The results show that

the failure of the flange plate was mainly caused by the continuous pitting corrosion and dissolved corrosion in high temperature and pressure urea corrosive medium.The interface between the corrosive medium and flange plate was serrated and the corrosion products were mainly Fe and Cr oxides.Loose structure and a large number of holes and cracks appeared in the corrosion products.The TP304 austenitic stainless steel is unsuitable for the seal flange material for urea hydrolysis equipment in flue gas denitrificaiton.

关键词

Keywords

references

Views

150

下载量

CSCD

Alert me when the article has been cited

提交

Publicity Resources

ANALYSIS OF REPAIR WHEN LEAKAGE OCCURRED ON FOUR KINDS OF TUBES IN THE BOILER OF 300MW UNIT

Pitting corrosion behavior of TP304 stainless steel in urban reclaimed water

PROBLEMS EXISTING IN OPERATION OF WET LIMESTONE/GYPSUM DESULFURATION SYSTEM IN LUOHUANG POWER PLANT AND ANALYSIS THEREOF

CAUSE ANALYSIS OF WATER-WALL TUBE BURST AND LEAKAGE FOR A 2100t/h BOILER

CAUSE ANALYSIS OF CORROSION FOR CHEMICAL-DOSING TUBE ENTERING INTO THE DRUM PORT

Related Author

LONG Huiguo

LONG Yi

CHEN HongdongHunan Provincial Electric Power Testing & Research Institute

ZHANG Guiquan

LIU Feng

LIN He

ZHANG Heng

WEN Huifeng

Related Institution

Hunan Electric Power Test and Research Institute

Huaneng Hainan Power Generation Co., Ltd. Dongfang Power Plant

Chongqing Electric Power College Chongqing

Shajiao C Power Plant

Guangdong Electric Power Test and Research Institute Dongguan

AI问答

⁰