Experimental study on morphology and mineral composition of slag from a Zhundong coal-fired power plant

Thermal Power Generation Vol. 44, Issue 7, Pages: 18-22(2015)

更新时间：2025-09-28

- Experimental study on morphology and mineral composition of slag from a Zhundong coal-fired power plant
- 作者机构：
  
  1. 湛江中粤能源有限公司
  2. 西安热工研究院有限公司
  3. 华中科技大学能源与动力工程学院
- 作者简介：
- 基金信息：
- DOI：
  CLC： TM621.2
- Published：2015
- 稿件说明：
移动端阅览
FU Yongqiang, WANG Huajian, LI Kui, et al. Experimental study on morphology and mineral composition of slag from a Zhundong coal-fired power plant[J]. Thermal Power Generation, 2015, 44(7): 18-22.
DOI：

FU Yongqiang, WANG Huajian, LI Kui, et al. Experimental study on morphology and mineral composition of slag from a Zhundong coal-fired power plant[J]. Thermal Power Generation, 2015, 44(7): 18-22. DOI：

摘要

准东煤易着火、燃尽率高

是优良的动力用煤

但其严重的沾污结渣特性严重影响电厂锅炉安全运行。为此

采用X射线衍射仪和环境扫描电子显微镜等

对燃用准东煤电厂锅炉各部位渣样的形貌和矿物组成特征进行了研究。结果表明:锅炉各部位渣样均含有复杂的钠矿物成分

包括钠钙铝氧化物的复杂矿物晶体、钠钾铝硅酸盐、霞石、钠钙铝硅酸盐等;锅炉高温区渣样中识别出大量的非晶组分

这源于各种矿物在高温区的共熔反应;锅炉低温换热面渣样则主要是积灰和沾污样

其含晶形矿物较多

这源于高温区气相组分的冷凝。

Abstract

Zhundong coal is easy to burn with a high burn out rate

which is a good coal for power plants.However

the serious fouling and slag occurred on heating surface of the boiler causes serious problems for unit safe operation.In this paper

the slag and deposition samples were collected from a power plant firing Zhundong coal.The X-ray diffraction and environmental scanning electron microscope(ESEM)was applied to analyze the mineral composition of the depositions.The results indicate that

the depositions collected from different parts of the boiler have complex Na-containing mineral components

including sodium calcium aluminum oxides mineral crystal

sodium potassium aluminum silicate

nelpheline

and sodium calcium aluminum silicate.A lot of amorphous components were identified in high temperature area

which is mainly derived from the eutectic reaction of various minerals.Mineral crystals were mainly found in fouling and deposit samples

which was mainly due to the condensation of gas phase.

关键词

Keywords

references

Views

319

下载量

CSCD

Alert me when the article has been cited

提交

Publicity Resources

Reaction kinetics study on SO3 formation with presence of sodium in the coal

Experiments about co-firing shale with Zhundong coal in a 100 MW unit boiler

Evaluation method for ash fouling characteristics of coals with high alkali content

Investigation on slagging problem occurred on a 350MW boiler co-fring Zhundong coal

Structure optimization for pulverized coal mixer of a 300 MW unit boiler

Related Author

GAO Manda

SUN Baomin

DING Shixing

ZHAO Bing

WANG Jiarui

WANG Penghui

CHEN Fanmin

QIN Ling

Related Institution

Key Laboratory of Condition Monitoring and Control for Power Plant Equipment, Ministry of Education, North China Electric Power University,, Chin

Huadian Electric Power Research Institute

Xinlian Coal Chemical Industry and Trade Co., Ltd.

Fengtai Power Generation Co., Ltd., Fengtai

Xi’an Thermal Power Research Institute Co., Ltd.

AI问答

⁰