Surface properties and flue gas denitrification performance of honeycomb CuO/γ-Al<sub>2</sub>O<sub>3</sub> catalysts

WANG Xuetao; JIAO Yefan; ZHUANG Shali; ZHANG Xingyu

English

您当前的位置：

首页 >

文章列表页 >

Surface properties and flue gas denitrification performance of honeycomb CuO/γ-Al₂O₃ catalysts

Thermal Power Generation Vol. 43, Issue 2, Pages: 30-35(2014)

更新时间：2025-09-28

- Surface properties and flue gas denitrification performance of honeycomb CuO/γ-Al₂O₃ catalysts
- 作者机构：
  
  河南科技大学车辆与动力工程学院
- 作者简介：
- 基金信息：
- DOI：
  CLC： TQ426;X701
- Published：2014
- 稿件说明：
移动端阅览
WANG Xuetao, JIAO Yefan, ZHUANG Shali, et al. Surface properties and flue gas denitrification performance of honeycomb CuO/γ-Al₂O₃ catalysts[J]. Thermal Power Generation, 2014, 43(2): 30-35.
DOI：

WANG Xuetao, JIAO Yefan, ZHUANG Shali, et al. Surface properties and flue gas denitrification performance of honeycomb CuO/γ-Al₂O₃ catalysts[J]. Thermal Power Generation, 2014, 43(2): 30-35. DOI：

摘要

通过浸渍法制备了CuO/γ-Al2O3系列催化剂

在模拟烟气脱硝试验装置上考察该催化剂的脱硝性能

并利用比表面积分析仪(BET)、X射线衍射(XRD)对催化剂进行了微观表征分析

研究了CuO的负载量、煅烧温度及CeO2对催化剂表面性能及催化剂脱硝活性的影响。结果表明:随着负载量的增加

CuO的衍射特征峰强度随之增加;CuO负载量对CuO/γ-Al2O3催化剂的表面结构有较大影响

随着CuO负载量的增加

试样的比表面积和孔体积均呈减小趋势

而平均孔径略微增大;CuO/γ-Al2O3催化剂的活性较高

对NO选择性催化还原较为适宜;CuO负载量为7.5%

煅烧温度为500℃时催化剂的NO转化率最高可达91.4%

加入CeO2可使催化剂的NO脱除效率达到94.5%。

Abstract

A series of CuO/γ-Al2O3 catalysts were prepared by impregnation method.The denitrification property of the catalysts was investigated in a simulated flue gas denitrification experimental device.The prepared samples were characterized by the BET specific surface area analyzer and X-ray diffraction(XRD).The effect of CuO loading

calcined temperature

and promoter CeO2 on catalytic performance was investigated.The XRD results showed that the intensity of X-rays diffraction pattern of CuO wais enhanced with the CuO loading amount.The BET results indicated that the CuO loading amount had a great influence on surface structure of the CuO/γ-Al2O3 catalyst.With the increasing CuO loading amount

the specific surface area and pore volume samples showed a decrease tendency while the average pore size slightly increased.The CuO/γ-Al2O3 catalyst had higher catalytic activity

which was suitable to the selective catalytic reduction of NO.The catalyst calcined at 500℃and loaded CuO with 7.5% had better catalysts morphology

and its denitrification efficiency can reach 91.4%.Addition of CeO2 can enhance the denitrification efficiency to 94.5%.

关键词

Keywords

references

Views

168

下载量

CSCD

Alert me when the article has been cited

提交

Publicity Resources

Review of study on catalysts for selective catalytic oxidation of NO in flue gas

Deactivation prediction model for flue gas denitration catalyst V-W-TiO₂

Experimental study on selective catalytic reduction of NO at low temperature by active carbon fibers supported copper oxide and zirconium catalyst

Comparison of effects of ammonium peroxydisulfate and sodium carbonate on regeneration of arsenic poisoned catalysts

APPLICATION OF SCR DENITRIFICATION TECHNOLOGY ONTO COAL-FIRED BOILERS IN CHINA

Related Author

ZHAO Tingwen

YAO Mingyu

FU Kangli

CHENG Guangwen

YANG Song

LI Yang

CAI Ming

SHEN Boxiong

Related Institution

Xi'an Thermal Power Research Institute Co., Ltd

College of Energy and Environmental Engineering, Hebei University of Technology

Datang Nanjing Environmental Protection Technology Co., Ltd

Department of Energy and Power Engineering, Henan University of Science and Technology

School of Chemistry and Chemical Engineering, South China University of Technology

AI问答

⁰

Surface properties and flue gas denitrification performance of honeycomb CuO/γ-Al2O3 catalysts

DOI：

摘要

Abstract

关键词

Keywords

references

Surface properties and flue gas denitrification performance of honeycomb CuO/γ-Al₂O₃ catalysts