CAUSE ANALYSIS OF FRACTURE OCCURRED ON THERMOWELL TO OUTLET HEADER OF THE PLATEN SUPERHEATER

JIN Feng; SONG Li; ZHANG Wuneng; WANG RuiHenan Electric Power Testing & Research Inatitute

English

您当前的位置：

首页 >

文章列表页 >

CAUSE ANALYSIS OF FRACTURE OCCURRED ON THERMOWELL TO OUTLET HEADER OF THE PLATEN SUPERHEATER

Thermal Power Generation Vol. 39, Issue 4, Pages: 100-101(2010)

更新时间：2025-09-28

- CAUSE ANALYSIS OF FRACTURE OCCURRED ON THERMOWELL TO OUTLET HEADER OF THE PLATEN SUPERHEATER
- 作者机构：
  
  河南电力试验研究院
- 作者简介：
- 基金信息：
- DOI：
  CLC： TK223.32
- Published：2010
- 稿件说明：
移动端阅览
JIN Feng, SONG Li, ZHANG Wuneng, et al. CAUSE ANALYSIS OF FRACTURE OCCURRED ON THERMOWELL TO OUTLET HEADER OF THE PLATEN SUPERHEATER[J]. Thermal Power Generation, 2010, 39(4): 100-101.
DOI：

JIN Feng, SONG Li, ZHANG Wuneng, et al. CAUSE ANALYSIS OF FRACTURE OCCURRED ON THERMOWELL TO OUTLET HEADER OF THE PLATEN SUPERHEATER[J]. Thermal Power Generation, 2010, 39(4): 100-101. DOI：

摘要

对某发电公司2号炉屏式过热器(屏过)出口集箱热电偶套管断裂原因进行了分析

结果表明热电偶套管的不合理结构加剧了热电偶套管断裂部位温度的升高和在交变应力下的振动使材料组织的快速老化以及焊接引起的σ相的存在共同导致了热电偶套管断裂。对此

建议在热电偶套管内壁加工内螺纹

使其结构更加稳定可靠

以避免同类事故发生。

Abstract

The causes of fracture on thermowell to outlet header for boiler no.2 in one power generation company have been analysed

results show that the causes leading to fracture are as follows:unreasonable structure of the thermowell has intensified the temperature rise and vibration under cyclic stress at location of fracture appeared on the thermowell

the existence of σ-phase due to rapid ageing of material texture and welding leads to fracture of the thermowell.For this

it is recommended to fabricate intermal thread on inner wall of the thermowell

making its structure to be more stable and reliable

to avoid occurrence of similar accidents.

关键词

Keywords

references

Views

下载量

CSCD

Alert me when the article has been cited

提交

Publicity Resources

MEASUREMENT AND ANALYSIS OF HEAT TRANSFER COEFFICIENT FOR PLATEN HEATING SURFACE IN CFB BOILERS

ANALYSIS AND TREATMENT OF FREQUENT TUBEBURST FOR LOW-TEMPERATURE REHEATER OF DG 1025 t/h BOILER

CAUSES LEADING TO OVER-TEMPERATURE OF SUPERHEATER FOR BOILERS OF SUPERCRITICAL 600MW UNITS AT INITIAL STAGE OF START-UP AND CONTROL THEREOF

CAUSE ANALYSIS OF SPACING TUBE BURST ON PLATEN SUPERHEATER OF ONE SUPERCRITICAL BOILER AND COUNTERMEASURES THEREOF

RETROFIT OF PLATEN SUPERHEATER FOR CFB BOILERS

Related Author

凌晓聪

吕俊复

刘青

王昕

张建胜

岳光溪

沈解忠

苏小平

Related Institution

Tsinghua University

Wuxi Boiler Factory

Harbin Boiler Factory

Harbin Boiler Factory Beijing

AI问答

⁰