CAUSE ANALYSIS OF IMPELLER FRACTURE FOR SLURRY-RECIRCULATING PUMPS IN SHANWEI POWER PLANT

HUANG Yi-huiRed Bay Power Generation Co Ltd

English

您当前的位置：

首页 >

文章列表页 >

CAUSE ANALYSIS OF IMPELLER FRACTURE FOR SLURRY-RECIRCULATING PUMPS IN SHANWEI POWER PLANT

Thermal Power Generation Vol. 39, Issue 2, Pages: 65-68(2010)

更新时间：2025-09-28

- CAUSE ANALYSIS OF IMPELLER FRACTURE FOR SLURRY-RECIRCULATING PUMPS IN SHANWEI POWER PLANT
- 作者机构：
  
  红海湾发电有限公司
- 作者简介：
- 基金信息：
- DOI：
  CLC： TH31
- Published：2010
- 稿件说明：
移动端阅览
HUANG Yi-huiRed Bay Power Generation Co Ltd. CAUSE ANALYSIS OF IMPELLER FRACTURE FOR SLURRY-RECIRCULATING PUMPS IN SHANWEI POWER PLANT[J]. Thermal Power Generation, 2010, 39(2): 65-68.
DOI：

HUANG Yi-huiRed Bay Power Generation Co Ltd. CAUSE ANALYSIS OF IMPELLER FRACTURE FOR SLURRY-RECIRCULATING PUMPS IN SHANWEI POWER PLANT[J]. Thermal Power Generation, 2010, 39(2): 65-68. DOI：

摘要

汕尾电厂1号、2号600 MW机组锅炉配套的石灰石/石膏湿法烟气脱硫(FGD)装置吸收塔浆液循环泵叶轮先后发生严重断裂

经过金相检验、化学成分分析及硬度检测等认为

其主要原因是吸收塔浆液的低pH值造成叶轮叶片基体腐蚀

降低了叶轮强度。另外

浆液对叶轮的磨损进一步加快了叶轮的断裂。对此

建议运行中控制吸收塔浆液的pH值

消除泵的气蚀现象

选择强度和韧性高及抗腐蚀性强的材料制造叶轮

泵的转速设计在450~530 r/min之间。

Abstract

Severe fracture of impeller had successively occurred in slurry-recirculating pumps equipped for the Absorption tower of lime-stone/gypsum wet flue gas desulphurization(FGD) system for boilers of 600 MW units NO.1 and NO.2 in Shanwei Power Plant.Through metallographic examination

chemical composition analysis

and hardness test etc.

it is believed that the cause leading to base corrosion of impeller blades is the low pH value of slurry from the Absorption tower

reducing the strength of impeller.In addition

the abrasion of slurry further accelerates the fracture of impeller.For this

it is recommented to control the pH value of slurry from the Absorption tower

eliminating cavitation phenomenon in the pumps

selecting materials with high strength

high toughness

and strong corrosion-resisting property for manufacturing the impeller

as well as the rotational speed of pumps should be designed within 450~530 r/min.

关键词

Keywords

references

Views

143

下载量

CSCD

Alert me when the article has been cited

提交

Publicity Resources

Reason analysis for the fifth stage blade fracture in low pressure cylinder of a 600MW unit steam turbine

Influence of water quality of circulating water on corrosion of materials in SCAL indirect air cooling system

PROBLEMS EXISTING IN OPERATION OF WET LIMESTONE/GYPSUM DESULFURATION SYSTEM IN LUOHUANG POWER PLANT AND ANALYSIS THEREOF

CAUSE ANALYSIS OF CORROSION FOR CHEMICAL-DOSING TUBE ENTERING INTO THE DRUM PORT

ANALYSIS OF “UNSYMMETRIC BURNING” PROBLEM IN A W-SHAPED FLAME BOILER OF 600 MW UNIT

Related Author

ZHANG Yonghai

XIAO Junfeng

GU Weiwei

YU Xiaobing

ZHU Baotian

CUI Xionghua Xi'an Thermal Power Research Institute Co.

XIAO Haigang

HUANG Wanqi

Related Institution

Xi'an Thermal Power Research Institute Co., Ltd

Ningxia Jingneng Ningdong Power Generation Co., Ltd

Chongqing Electric Power College Chongqing

Shengli Power Plant Dongying

Shandong Electric Power Research Institute

AI问答

⁰