Fracture failure analysis of Ni-based bolts for ultra-supercritical units
Thermal Power Generation   Issue 12, (2015)
更新时间：2025-09-28

    • Fracture failure analysis of Ni-based bolts for ultra-supercritical units

    • CLC： TM621

    • Published Online：15 January 2016，

      Published：2015

    移动端阅览

  • JIANG Tao, WANG Jianguang, ZHANG Zhibo, et al. Fracture failure analysis of Ni-based bolts for ultra-supercritical units[J]. Thermal Power Generation, 2015, (12). DOI：

  •  
  •  
icon
试读结束，您可以激活您的VIP账号继续阅读。
去激活 >
icon
试读结束，您可以通过登录账户，到个人中心，购买VIP会员阅读全文。
已是VIP会员？
去登录 >

0

Views

647

下载量

0

CSCD

Alert me when the article has been cited
提交
Outline
No Sections

Related Articles

Fracture analysis for dissimilar metal welded joints of 12Cr1MoVG/TP347H in a utility boiler
Reason analysis for fracture occurred in axial induced draft fan blade of a 600 MW unit
Thermal fatigue failure analysis for drainage-tank in hot section of reheat pipeline in an ultra supercritical 1 000 MW unit
Failure analysis and improvement for containment spray system valve's remote actuating mechanism in a nuclear power station
EQUIPMENTS' MANAGEMENT AND REPAIR OF 660MW UNITS IN SHAJIAO C POWER PLANT

Related Author

ZHANG Zonglai
SHI Zhigang
YU Xiaobing
LI Yuan
ZHANG Yonghai
GU Weiwei
LOU Yumin
PENG Yichao

Related Institution

Shenhua Guoneng Energy Group Corporation Limited
Xi’an Thermal Power Research Institute Co., Ltd.
Xi’an TPRI Energy Conservation Technology Co., Ltd.
Zhejiang Zhoushan Coal-based Power Co., Ltd.
0