CAUSE ANALYSIS OF REINFORCING WIRES FAILURE FOR INCOMING GAS SAFETY ISOLATING STRAINER OF THE GAS TURBINE

CHEN Peng; GAN Meng-bi; GAO Yan et al

doi:10.19666/j.rlfd.2004.12.015

English

您当前的位置：

首页 >

文章列表页 >

CAUSE ANALYSIS OF REINFORCING WIRES FAILURE FOR INCOMING GAS SAFETY ISOLATING STRAINER OF THE GAS TURBINE

Thermal Power Generation Issue 12, Pages: 48-50(2004)

更新时间：2025-09-28

- CAUSE ANALYSIS OF REINFORCING WIRES FAILURE FOR INCOMING GAS SAFETY ISOLATING STRAINER OF THE GAS TURBINE
- 作者机构：
  
  1. 月亮湾燃机电厂
  2. 华南理工大学,广东,深圳,518052
  3. ,广东,广州,510641
- 作者简介：
- 基金信息：
- DOI：10.19666/j.rlfd.2004.12.015
  CLC： TK47
- Published：2004
- 稿件说明：
移动端阅览
CHEN Peng, GAN Meng-bi, GAO Yan et al. CAUSE ANALYSIS OF REINFORCING WIRES FAILURE FOR INCOMING GAS SAFETY ISOLATING STRAINER OF THE GAS TURBINE[J]. Thermal Power Generation, 2004, (12): 48-50.
DOI：

CHEN Peng, GAN Meng-bi, GAO Yan et al. CAUSE ANALYSIS OF REINFORCING WIRES FAILURE FOR INCOMING GAS SAFETY ISOLATING STRAINER OF THE GAS TURBINE[J]. Thermal Power Generation, 2004, (12): 48-50. DOI： 10.19666/j.rlfd.2004.12.015.

摘要

通过对月亮湾燃机电厂 3号燃机进气安全隔离滤网失效的不锈钢钢丝进行无损检测和其化学成分、金相、能谱以及断口分析等

确定不锈钢钢丝合金比例不当、锰含量太高且晶间析出碳化物 ;材质存在严重质量问题。建议钢丝材料选用超低碳、铬镍含量高、含钼 2 %～ 3 %的 0 0Cr1 7Ni1 4Mo3或 3 1 6L( 0 0Cr1 7Ni1 4Mo2 )奥氏体不锈钢

且制造应符合GB 4 2 4 0要求

Abstract

Throung tests of non-destructive detection

analysis of chemical composition

metallurgy

energy spectrum

and fractures for the failed reinforcing wires of incoming gas safety isolating strainer on gas turbine No.3 in Yueliangwan Gas Tubine Power Plant

it is determined that one cause leading to early fracture is unsuitable proportion of alloy composition for the stainless wires

the content of mangonese being high

eduction of intergranular carbide

as well as sirious quality problems existing in the material used. It is recommended to select OOCr 17 Ni14 Mo3 or 316L (OOCr17N:14MoZ) austenitic stainless steel having ultta-low carbon content

high Cr and Ni content

and 2%～3%Mo content

and the fabrication of reinforcing wires having to be in conformity with requirements of standard GB4240.

关键词

Keywords

references

Views

下载量

CSCD

Alert me when the article has been cited

提交

Publicity Resources

STUDY ON SERVICING BEHAVIOR OF BOILER TUBES MADE FROM 18-8 TYPE AUSTENITIC STAINLESS STEEL(6)

STUDY ON VELOCITY UNIFORMITY IN INLET FLUE DUCT OF HEAT RECOVERY BOILER FOR LARGE-SCALE GAS TURBINE

MEASURES FOR REDUCING UNCERTAINTY IN INTEGRATED PERFORMANCE TEST OF COMBINED CYCLE UNIT

HEAT,ELECTRICITY AND COOL TRIPLE CO-GENERATION SCHEME BY USING NATURAL GAS FOR RESIDENTIAL QUATERS AND ANALYSIS OF ITS TECHNOECONOMIC PERFORMANCE

A SUMMARY AND PROSPECTS OF STUDY ON START-UP PROCESS FOR GAS TURBINES

Related Author

MA Hong

ZHANG Lei

ZHENG Fangping

HE Xipeng

SHI Zhigang

WANG Hongzhe Xi'an Thermal Power Research Institute Co Ltd

ZHAO Jian-yun

PAN Wei

Related Institution

Xi'an Thermal Power Research Institute Co., Ltd

Zhejiang University

Hangzhou Boiler Group Co., Ltd

Xi'an Thermal Power Research Institute Co.,Ltd.

Nanjing University of Technology

AI问答

⁰