APPLICATION OF MAGNETIC MEMORY METHOD IN STRESS STATE DETECTION OF FILLET WELD JOINT ON TUBE SOCKET CONTAINING DEFECTS EXCEEDING GRADE

XU Hao-hao; QIU Jun; JIN Jie

doi:10.19666/j.rlfd.2006.02.014

English

您当前的位置：

首页 >

文章列表页 >

APPLICATION OF MAGNETIC MEMORY METHOD IN STRESS STATE DETECTION OF FILLET WELD JOINT ON TUBE SOCKET CONTAINING DEFECTS EXCEEDING GRADE

Thermal Power Generation Issue 2, Pages: 45-46(2006)

更新时间：2025-09-28

- APPLICATION OF MAGNETIC MEMORY METHOD IN STRESS STATE DETECTION OF FILLET WELD JOINT ON TUBE SOCKET CONTAINING DEFECTS EXCEEDING GRADE
- 作者机构：
  
  1. 嘉兴发电有限责任公司
  2. 浙江省火电建设公司
- 作者简介：
- 基金信息：
- DOI：10.19666/j.rlfd.2006.02.014
  CLC： TG441.7
- Published：2006
- 稿件说明：
移动端阅览
XU Hao-hao, QIU Jun, JIN Jie. APPLICATION OF MAGNETIC MEMORY METHOD IN STRESS STATE DETECTION OF FILLET WELD JOINT ON TUBE SOCKET CONTAINING DEFECTS EXCEEDING GRADE[J]. Thermal Power Generation, 2006, (2): 45-46.
DOI：

XU Hao-hao, QIU Jun, JIN Jie. APPLICATION OF MAGNETIC MEMORY METHOD IN STRESS STATE DETECTION OF FILLET WELD JOINT ON TUBE SOCKET CONTAINING DEFECTS EXCEEDING GRADE[J]. Thermal Power Generation, 2006, (2): 45-46. DOI： 10.19666/j.rlfd.2006.02.014.

摘要

用磁记忆检测(MMT)法评价了含超标缺陷管座角焊缝长期服役后的应力集中状况。通过对含超标缺陷管座与其它管座焊缝及预制受损试样残余应力水平的比较

认为超标缺陷尚处于稳定状态

为含超标缺陷管座的运行监督提供了依据。

Abstract

The stress concentration state of weld joint on a tube socket containing defects exceeding grade after long term service has been evaluated by using the magnetic memory test (MMT). Throwgh comparison of weld joints on tube socket containing defects exceeding grade and on other tube socket

as well as the residual stress levels of prefabricated damaged samples

it is believed that the defects containing exceeding grade are still in a stable condition

providing basis for operating supervision of tube sockets containing defects exceeding grade.

关键词

Keywords

references

Views

104

下载量

CSCD

Alert me when the article has been cited

提交

Publicity Resources

CRACKING OF MEDIUM-AND SMALL-DIAMETER TUBE SOCKETS ON HIGH TEMPERATURE STEAM PIPELINES AND HEADERS, AS WELL AS PROTECTIVE MEASURES THEREOF

Related Author

WANG Bin

Related Institution

Boiler and Pressure Vessel Inspection Center of Gansu Electric Power Company

AI问答

⁰