CAUSE ANALYSIS OF TUBE-BURST ON PLATEN SUPERHEATER

ZHANG Xiao-yu1; YANG Jian-ju1; OUYANG Jie1; ZHAO Su-fen21.Hebei Provincial Electric Power Research Institute

doi:10.19666/j.rlfd.2007.12.023

English

您当前的位置：

首页 >

文章列表页 >

CAUSE ANALYSIS OF TUBE-BURST ON PLATEN SUPERHEATER

Thermal Power Generation Issue 12, Pages: 83-85(2007)

更新时间：2025-09-28

- CAUSE ANALYSIS OF TUBE-BURST ON PLATEN SUPERHEATER
- 作者机构：
  
  1. 河北省电力研究院
  2. 华电石家庄热电有限公司
- 作者简介：
- 基金信息：
- DOI：10.19666/j.rlfd.2007.12.023
  CLC： TK223.32;TK228
- Published：2007
- 稿件说明：
移动端阅览
ZHANG Xiao-yu1, YANG Jian-ju1, OUYANG Jie1, et al. CAUSE ANALYSIS OF TUBE-BURST ON PLATEN SUPERHEATER[J]. Thermal Power Generation, 2007, (12): 83-85.
DOI：

ZHANG Xiao-yu1, YANG Jian-ju1, OUYANG Jie1, et al. CAUSE ANALYSIS OF TUBE-BURST ON PLATEN SUPERHEATER[J]. Thermal Power Generation, 2007, (12): 83-85. DOI： 10.19666/j.rlfd.2007.12.023.

摘要

通过采用化学成分分析、宏观检验和显微组织分析等方法对石家庄热电有限公司屏式过热器爆管试样进行了分析

并通过氧化皮厚度估算了其当量温度

计算出屏式过热器剩余寿命。分析认为屏式过热器爆管为长时间超温运行

造成材料组织老化及腐蚀引起

建议运行中加强高温金属部件入厂检验、在线监测及寿命评估等

以确保机组安全运行。

Abstract

Through methods

such as chemical composition analysis

macroscopic examination

and microstructure analysis etc.

the causes resulting in tube-burst on platen superheater in Shijiazhuang Thermal Power Co Ltd have been analysed

the equivalent temperature being estimated through thickness of the oxide skin

and residual service life being calculated. It is recommended to strengthen the plant-incoming inspection of high-temperature metallic parts

on-line monitoring

and service life evaluation etc.

so as to ensure safe operation of the unit.

关键词

Keywords

references

Views

下载量

CSCD

Alert me when the article has been cited

提交

Publicity Resources

SERVICE LIFE EVALUATION FOR HIGH TEMPERATURE PIPELINE IN POWER PLANTS BASED ON DAMAGE MECHAINCS

ANALYSIS OF SUPERHEATER'S TUBE-BURST CAUSED BY FALLING-AWAY OF OXIDE SKIN

EVALUATION OF SERVICE LIFE CONCERNING HEATING SURFACE OF BOILER NO.1 IN HUANENG HUAIYIN POWER PLANT

CAUSE ANALYSIS AND COUNTERMEASURES FOR BURST-CRACKING OF PLATEN SUPERHEATER OF BOILER NO.1

ANALYSIS OF MECHNISMS FOR OXIDE SKIN FORMATION AND EXFOLIATION IN SUPERHEATER OF SUPERCRITICAL BOILERS AS WELL AS PREVENTIVE MEASURES THEREOF

Related Author

YANG Jian-hua

ZHU Jing-song

CUI Chao-ying

LI Yao-jun

ZHU Jianhua

GAO Shang-de

XUE Jia-lin

ZHANG Min-qi

Related Institution

Zhengzhou Electric Power Vocational College, Zhengzhou Electric Power Vocational College, Zhengzhou Electric Power Vocational College Henan Zhengzhou 450004, Zhengzhou 450004

Xi'an Thermal Power Research Institute Co.,Ltd.

Huaneng Huaiyin Power Plant

Hancheng Power Plant

Guohua Taicang Power Plant

AI问答

⁰