JIN Qijie; TAO Xingjun; PAN Youchun; SHEN Yuesong; ZHU Shemin

doi:10.19666/j.rlfd.201705036

English

您当前的位置：

首页 >

文章列表页 >

Effect of Y³⁺ and La³⁺ on catalytic performance of CeO₂(ZrO₂)/TiO₂ catalyst during selective catalytic reduction of NO_x

Thermal Power Generation Vol. 47, Issue 2, Pages: 71-77(2018)

更新时间：2025-09-28

- Effect of Y³⁺ and La³⁺ on catalytic performance of CeO₂(ZrO₂)/TiO₂ catalyst during selective catalytic reduction of NO_x
- 作者机构：
  
  1. 南京工业大学材料科学与工程学院
  2. 南京工业大学江苏先进无机功能复合材料协同创新中心
- 作者简介：
- 基金信息：
- DOI：10.19666/j.rlfd.201705036
  CLC： TB34
- Published Online：31 January 2018，
  
  Published：2018
- 稿件说明：
移动端阅览
JIN Qijie, TAO Xingjun, PAN Youchun, et al. Effect of Y³⁺ and La³⁺ on catalytic performance of CeO₂(ZrO₂)/TiO₂ catalyst during selective catalytic reduction of NO_x[J]. Thermal Power Generation, 2018, 47(2): 71-77.
DOI：

JIN Qijie, TAO Xingjun, PAN Youchun, et al. Effect of Y³⁺ and La³⁺ on catalytic performance of CeO₂(ZrO₂)/TiO₂ catalyst during selective catalytic reduction of NO_x[J]. Thermal Power Generation, 2018, 47(2): 71-77. DOI： 10.19666/j.rlfd.201705036.

摘要

采用溶胶-凝胶法制备Y~(3+)和La~(3+)掺杂CeO_2(ZrO_2)/TiO_2(简称CZT)催化剂

研究Y~(3+)和La~(3+)掺入对其脱硝性能的影响。采用X射线衍射、氮气吸附脱附、氨气程序升温吸附、氢气程序升温还原以及紫外光光致发光光谱等实验方法对CZT催化剂进行表征。结果表明:Y~(3+)和La~(3+)的掺入抑制了TiO_2从无定形向锐钛矿型转变

不仅增大了催化剂的弱酸酸量和比表面积

同时提高了CZT催化剂的缺陷浓度和储释氧性能;弱酸酸量和比表面积的增大有利于CZT催化剂表面反应气体的吸附;缺陷浓度和储释氧性能的提高加快了吸附在CZT催化剂表面的NO被氧化速率

有利于催化反应的进行。因此

适量掺入Y~(3+)和La~(3+)会明显提升CZT催化剂的低温脱硝活性

拓宽其活性温度窗口。空速71 400 h-1条件下

0.2LaCZT催化剂在200℃的脱硝率达到85.1%

300℃达到最高(96.5%)。

Abstract

A series CeO_2(ZrO_2)/TiO_2 catalysts(CZT catalyst) were modified with Y~(3+) and La~(3+) using the sol-gel method. The effect of Y~(3+) and La~(3+) on catalytic performance of the CeO_2(ZrO_2)/TiO_2 during selective catalytic reduction(SCR) of NOx using NH3 was investigated. Several tests were carried out the characterize the CZT catalysts

such as the X-ray diffraction

nitrogen adsorption and desorption

temperature programmed desorption of ammonia

temperature programmed reduction of hydrogen and photoluminescence spectra. The results show that

the addition of Y~(3+) and La~(3+) inhibited the transformation of TiO_2 from amorphous phase to anatase phase. In addition

both Y~(3+) and La~(3+) ions increased the specific surface area and amount of weak acid sites in the catalysts

which was beneficial for the adsorption of reaction gas on the catalyst surface. The increase of the defects species concentration and the enhancement of oxygen storage capacity was good for catalytic activity. Therefore

the additions of Y~(3+) and La~(3+) improved the catalytic activity of the catalyst at low temperatures and broadened the active temperature window while the amount was appropriate. Under condition with GHSV of 71 400 h-1

the catalytic activity(NOx conversion rate) of the 0.2 La-CZT catalyst reached 85.1% at 200 ℃ and 96.5 % at 300 ℃(the highest).

关键词

Keywords

references

Views

106

下载量

CSCD

Alert me when the article has been cited

提交

Publicity Resources

APPLICATION OF SCR DENITRIFICATION TECHNOLOGY ONTO COAL-FIRED BOILERS IN CHINA

STUDY ON BEHAVIOR OF CATALYCTS FOR SCR DENITRIFICATION USING DIFFERENT TiO₂ AS CARRIER

THE OPERATION SITUATION OF CATALYST IN SCR DENITRIFICATION SYSTEM OF ONE THERMAL POWER PLANT

TEST STUDY ON CATALYTIC PYROLYSIS OF RICE HUSKS IN A FIXED BED REACTOR

STUDY ON BEHAVIOR AND KINETICS OF CATALYTIC PYROLYSIS FOR RICE HUSK

Related Author

Hans Jensen-Holm1

Nan-yu Topsφe1

CUI Jian-hua21.Topsoe Company

ZHU Chong-bing

LI Feng

JIN Bao-sheng

CHENG Ling-xia South-east China University

ZHANG Qiang

Related Institution

Topso Company Beijing Representative Office

Topso Corporation

Southeast University

Xi'an Thermal Power Research Institute Co., Ltd

College of Basic Education, Shenyang University of Technology

AI问答

⁰