Effect of substrate hardness on microstructures and properties of cold-sprayed coatings

Thermal Power Generation Vol. 47, Issue 7, Pages: 93-98(2018)

更新时间：2025-09-28

- Effect of substrate hardness on microstructures and properties of cold-sprayed coatings
- 作者机构：
  
  西安热工研究院有限公司
- 作者简介：
- 基金信息：
- DOI：10.19666/j.rlfd.201710109
  CLC： O532
- Published Online：04 July 2018，
  
  Published：2018
- 稿件说明：
移动端阅览
LI Yong, LI Taijiang, LI Wei, et al. Effect of substrate hardness on microstructures and properties of cold-sprayed coatings[J]. Thermal Power Generation, 2018, 47(7): 93-98.
DOI：

LI Yong, LI Taijiang, LI Wei, et al. Effect of substrate hardness on microstructures and properties of cold-sprayed coatings[J]. Thermal Power Generation, 2018, 47(7): 93-98. DOI： 10.19666/j.rlfd.201710109.

摘要

为分析Co基合金材料用于冷喷涂修复不同硬度基材的可行性

在3种不同硬度的基体材料表面

采用冷喷涂工艺制备了Co基合金涂层

并进行了组织结构、硬度、冲蚀磨损性能以及抗腐蚀性能研究。结果表明:随着基体硬度的增加

Co基合金粉末颗粒变形更加明显;304不锈钢基体表面涂层的孔隙率低于Cu基体和司太立合金基体表面涂层的孔隙率;在司太立合金基体上的喷涂态Co基合金涂层硬度高于其他2种基体涂层的硬度;3种基体表面涂层的盐雾腐蚀和电化学腐蚀性能无明显差异

但其电化学腐蚀性能均优于各基体;Cu基体表面涂层受到30°攻角冲蚀磨损时

其质量损失比其他2种涂层高22%;但在90°攻角冲蚀磨损时

3种涂层质量损失相当;基体与冷喷涂粉末硬度的匹配影响涂层的组织和性能。

Abstract

To explore the repair probability of substrate with different hardness by Co-based materials for cold spraying

Co-based alloy coatings were deposited on three substrates with different hardness by cold spraying in this study. The microstructure

hardness

erosion and corrosion resistance of cold-sprayed coatings were characterized. The results show that

with the increase of substrate hardness

the deformation of Co-based alloy powder particles is more pronounced. Porosity of coatings sprayed on 304 stainless steel substrate is lower than that of coatings sprayed on Cu and Stellite substrates. Hardness of as-sprayed Co-based alloy coatings deposited on Stellite substrates is higher than that of the other two coatings. The three coatings exhibit similar salt fog corrosion and electrochemical corrosion properties. Moreover

the electrochemical corrosion properties of three coatings are better than three substrates. The erosion weight loss of coating deposited on Cu substrates is 22% higher than other coatings when subjected 30° erosion. The weight losses of three coatings are similar after 90° erosion test. The research results indicate that the matching of substrate with the hardness of cold spray powder affect the microstructure and properties of cold sprayed coatings.

关键词

Keywords

references

Views

160

下载量

CSCD

Alert me when the article has been cited

提交

Publicity Resources

Key technology of optimization reform of ultra low pressure economizer

PROBLEMS EXISTING IN OPERATION OF WET LIMESTONE/GYPSUM DESULFURATION SYSTEM IN LUOHUANG POWER PLANT AND ANALYSIS THEREOF

CAUSE ANALYSIS OF CORROSION FOR CHEMICAL-DOSING TUBE ENTERING INTO THE DRUM PORT

CAUSE ANALYSIS AND PROTECTIVE MEASURES FOR CORROSIVE PERFORATION OF CONDENSER’S COPPER TUBES IN YUNFU POWER PLANT

STUDY ON PERFORMANCE OF HIGH HARDNESS AND LOW HARDNESS WELD JOINTS ON P91 MAIN STEAM PIPE

Related Author

LI Nan

ZHANG Zhixiang

ZOU Xiaogang

CHE Hongwei

LU Jun

ZHOU Fei

LI Wenfeng

SHEN Jikang

Related Institution

Xi'an Xire Boiler Environmental Protection Engineering Co., Ltd

Chongqing Electric Power College Chongqing

Shengli Power Plant Dongying

Yunfu Power Plant Guangdong Yunfu

AI问答

⁰