Comparison of detection methods for cracks under coating of overflow components

WANG Peng; ZHU Hongbo; LIU Runbing; LI Dongjiang; QIN Chengpeng; HE Huchang; JIANG Xiong; WANG Qiang; LANG Tao

doi:10.19666/j.rlfd.201911250

English

您当前的位置：

首页 >

文章列表页 >

Comparison of detection methods for cracks under coating of overflow components

Thermal Power Generation Vol. 49, Issue 3, Pages: 113-117(2020)

更新时间：2025-09-28

- Comparison of detection methods for cracks under coating of overflow components
- 作者机构：
  
  1. 西安热工研究院有限公司
  2. 四川华能康定水电有限责任公司
  3. 华能糯扎渡电厂
- 作者简介：
- 基金信息：
- DOI：10.19666/j.rlfd.201911250
  CLC： O39
- Published Online：26 February 2020，
  
  Published：2020
- 稿件说明：
移动端阅览
WANG Peng, ZHU Hongbo, LIU Runbing, et al. Comparison of detection methods for cracks under coating of overflow components[J]. Thermal Power Generation, 2020, 49(3): 113-117.
DOI：

WANG Peng, ZHU Hongbo, LIU Runbing, et al. Comparison of detection methods for cracks under coating of overflow components[J]. Thermal Power Generation, 2020, 49(3): 113-117. DOI： 10.19666/j.rlfd.201911250.

摘要

水电站过流部件涂层下存在裂纹会直接导致部件抗疲劳强度下降

影响机组安全。为实现涂层下裂纹检测

本文在对比多种常用无损检测方法基础上

优选出涡流检测作为过流部件检测方法

并对3种涡流检测方法进行试验分析。结果表明:脉冲涡流检测的检出效率较低且易受裂纹方向的影响

很难满足现场快速检测的要求;交流磁场检测无法穿透涂层

不能进行裂纹检测;阵列涡流检测能有效检测涂层下裂纹

适用于现场实施的过流部件涂层下裂纹检测。

Abstract

Cracks under the coating of overcurrent components of hydropower station will directly lead to a decrease of the components' fatigue strength and affect the safety of the hydroelectric units. In order to realize crack detection under the coating

eddy current detection is selected as the detection method of over-current components in this paper

through comparison of multiple non-destructive detection methods. Three kinds of eddy current testing methods are analyzed. The results show that

the detection efficiency of pulsed eddy current testing is low and easy to be affected by the crack direction

which is difficult to meet the requirements of rapid detection on site. The ACFM testing can not penetrate the coating

and is not able to carry out crack detection. The array eddy current testing can effectively detect the cracks under the coating

which is suitable for the detection of cracks under the coating of overcurrent components on site.

关键词

Keywords

references

Views

下载量

CSCD

Alert me when the article has been cited

提交

Publicity Resources

SUPERSONIC TESTING OF P92 STEEL

STUDY ON DETECTION METHOD OF FIR-TREE BLADE ROOT ASSEMBLED ALONG AXIAL DIRECTION OF THE STEAM TURBINE

DUCTILITY AND TOUGHNESS VARYING TENDENCY OF T91-STEEL AFTER LONG-TIME OPERATING AT HIGH TEMPERTURE

Reason analysis on leakage of T92 steel tube in an ultra supercritical boiler and the countermeasures

Numerical analysis on stress intensity of austenite surfacing welding crack on BFP casing

Related Author

WANG Hongtao1

LI Jianmin2

LIU Yang21.Huaneng Qinbei Power Generation Co Ltd

GAO Lei1

LI Zhifa2

XUE Kaifeng1 1.Xi'an Thermal Power Research Institute Co Ltd

ZHANG Xiaoyu1

OU YangJie1

Related Institution

Huaneng Qinbei Power Generation Co., Ltd

Huaneng Chongqing Luohuang Power Generation Co., Ltd

Hebei Electric Power Science Research Institute

Guangdong Power Grid Corporation Electric Power Science Research Institute

Shanghai Electric Power Maintenance Factory Co., Ltd

AI问答

⁰