General corrosion behavior of T22 material in high temperature and high pressure water chemical environment

doi:10.19666/j.rlfd.201912259

English

您当前的位置：

首页 >

文章列表页 >

General corrosion behavior of T22 material in high temperature and high pressure water chemical environment

Thermal Power Generation Vol. 49, Issue 9, Pages: 93-97(2020)

更新时间：2025-09-28

- General corrosion behavior of T22 material in high temperature and high pressure water chemical environment
- 作者机构：
  
  1. 西安热工研究院有限公司
  2. 华能山东石岛湾核电有限公司
- 作者简介：
- 基金信息：
- DOI：10.19666/j.rlfd.201912259
  CLC： TM621.8
- Published Online：15 August 2020，
  
  Published：2020
- 稿件说明：
移动端阅览
General corrosion behavior of T22 material in high temperature and high pressure water chemical environment[J]. Thermal Power Generation, 2020, 49(9): 93-97.
DOI：

General corrosion behavior of T22 material in high temperature and high pressure water chemical environment[J]. Thermal Power Generation, 2020, 49(9): 93-97. DOI： 10.19666/j.rlfd.201912259.

摘要

本文在模拟高温气冷堆二回路的高温高压水化学环境下

研究了蒸汽发生器T22材质传热管在不同水化学环境中的均匀腐蚀行为。结果表明:提高溶液p H值、降低联氨质量浓度能够在一定程度上抑制T22材质的均匀腐蚀;随着反应温度升高

T22材质传热管均匀腐蚀速率加快;在高温高压水化学环境中

T22材质表面生成Fe3O4氧化膜

并随着反应时间的延长

Fe3O4晶粒尺寸逐渐长大

氧化膜致密性显著增加

导致T22材质均匀腐蚀速率显著降低

反应768 h后的T22材质均匀腐蚀速率降至0.016 g/(m2·h)。

Abstract

The general corrosion behavior of T22 material steam generator tube was studied in the simulating water chemical environment of secondary loop of high temperature gas cooled reactor. The results show that

the general corrosion of T22 material was inhibited to a certain extent by increasing the solution pH value and reducing the concentration of hydrazine. With the increase of reaction temperature

the general corrosion rate of T22 heat pipe was accelerated. In the high-temperature and high-pressure water chemical environment

Fe3 O4 oxide film was formed on the surface of T22

and Fe3 O4 grain size and compactness of oxide film increased significantly with the extension of reaction time

leading to a significant decrease in T22 general corrosion rate

which decreased to 0.016 0 g/（m2·h） after 768 hours’ reaction.

关键词

Keywords

references

Views

下载量

CSCD

Alert me when the article has been cited

提交

Publicity Resources

Experimental study on deposition law of corrosion products in throttle orifice of steam generator in high temperature gas cooled reactor

Effect of dissolved oxygen on deposition rules of corrosion products in orifice of steam generators

Cleaning schemes for the secondary circuit in high temperature gas-cooled reactors

Harmfulness analysis method for double ended break in main steam pipe of high temperature gas-cooled reactor

Influence of surface modification on steam oxidation of Super304H at 650 ℃

Related Author

姚建涛

龙国军

贾晶晶

吴志军

张贵泉

王威

LI Kang

YE Lin

Related Institution

Xi’an Thermal Power Research Institute Co., Ltd.

Huaneng Shandong Shidao Bay Nuclear Co., Ltd., Rongcheng

State Nuclear Electric Power Planning Design & Research Institute

Xi'an Thermal Power Research Institute Co.,Ltd.

Xi'an Technological University

AI问答

⁰