SCAL型间冷循环水水质对金属材料腐蚀影响

肖海刚; 黄万启; 汤自强; 王刚; 张洪博; 苏玮; 韩霜

doi:10.19666/j.rlfd.201904110

English

您当前的位置：

首页 >

文章列表页 >

SCAL型间冷循环水水质对金属材料腐蚀影响

热力发电 2019年48卷第12期页码：13-18

材料腐蚀与防护专栏 | 更新时间：2025-09-28

- SCAL型间冷循环水水质对金属材料腐蚀影响
- Influence of water quality of circulating water on corrosion of materials in SCAL indirect air cooling system
- 作者机构：
  
  1. 西安热工研究院有限公司
  2. 宁夏京能宁东发电有限责任公司
- 作者简介：
- 基金信息：
- DOI：10.19666/j.rlfd.201904110
  中图分类号： TK172
- 网络出版：2019-12-31，
  
  纸质出版：2019
- 稿件说明：
移动端阅览
肖海刚, 黄万启, 汤自强, 等. SCAL型间冷循环水水质对金属材料腐蚀影响[J]. 热力发电, 2019,48(12):13-18.

XIAO Haigang, HUANG Wanqi, TANG Ziqiang, et al. Influence of water quality of circulating water on corrosion of materials in SCAL indirect air cooling system[J]. Thermal Power Generation, 2019, 48(12): 13-18.
肖海刚, 黄万启, 汤自强, 等. SCAL型间冷循环水水质对金属材料腐蚀影响[J]. 热力发电, 2019,48(12):13-18. DOI： 10.19666/j.rlfd.201904110.

XIAO Haigang, HUANG Wanqi, TANG Ziqiang, et al. Influence of water quality of circulating water on corrosion of materials in SCAL indirect air cooling system[J]. Thermal Power Generation, 2019, 48(12): 13-18. DOI： 10.19666/j.rlfd.201904110.

摘要

目前

表面冷凝器铝换热器(SCAL)型间接空冷系统(间冷)循环冷却水的水质运行控制尚无标准可依

间冷循环水水质对系统金属材料腐蚀的影响也缺乏系统研究。本文根据间冷循环水水质特点

通过实验室模拟实验研究水中痕量SO_4~(2–)、Cl~–以及pH值等因素对碳钢和纯铝腐蚀的影响。结果表明:水中痕量(≤1 mg/L)的SO_4~(2–)和Cl~–均可加速碳钢腐蚀;SO_4~(2–)对碳钢腐蚀表现出自催化效应

同样质量浓度的SO_4~(2–)比Cl–对碳钢腐蚀危害更大

而SO_4~(2–)对纯铝表现出缓蚀作用;溶液pH值上升则会加速纯铝腐蚀。

Abstract

Currently

there is no standard for water quality control for circulating water in indirect air cooling system of surface condenser aluminum heat exchanger(SCAL). Additionally

study on the influence of water quality on the corrosion of materials in this system was scarce. To solve this problem

according to the characteristics of water quality of circulating water in this system

the influence of trace SO_4~(2–)

Cl~– and pH value on corrosion process of the carton steel and pure aluminum were experimentally investigated in laboratory. The results indicate that

trace SO_4~(2–) and Cl~– in the water(≤1 mg/L) could accelerate the corrosion process of the carbon steel. The SO_4~(2–) could be self-catalyzed during this process. Therefore

the harm of SO_4~(2–) was much larger than that of the Cl– with the same concentration. Furthermore

SO_4~(2–) could also reduce the corrosion of the pure aluminum

and the corrosion rate of aluminum increased with the pH value.

关键词

Keywords