- 盐雾环境下发电机定子停用防护技术
- Shutdown protection technology of generator stator in salt spray environment
- 作者机构：
  
  1. 国能(连江)港电有限公司
  2. 西安热工研究院有限公司
  3. 西安益通热工技术服务有限责任公司
- 作者简介：
- 基金信息：
- DOI：10.19666/j.rlfd.202107139
  中图分类号： TM31
- 纸质出版：2022
- 稿件说明：
移动端阅览
王珂, 张贵泉, 张兆, 等. 盐雾环境下发电机定子停用防护技术[J]. 热力发电, 2022,51(3):148-152.

WANG Ke, ZHANG Guiquan, ZHANG Zhao, et al. Shutdown protection technology of generator stator in salt spray environment[J]. Thermal Power Generation, 2022, 51(3): 148-152.
王珂, 张贵泉, 张兆, 等. 盐雾环境下发电机定子停用防护技术[J]. 热力发电, 2022,51(3):148-152. DOI： 10.19666/j.rlfd.202107139.

WANG Ke, ZHANG Guiquan, ZHANG Zhao, et al. Shutdown protection technology of generator stator in salt spray environment[J]. Thermal Power Generation, 2022, 51(3): 148-152. DOI： 10.19666/j.rlfd.202107139.

摘要

在模拟高湿度盐雾环境下，研究了发电机定子金属材质的腐蚀行为，并开发出了一套发电机定子充氮保养系统，在某电厂百万千瓦机组上开展了工业试验。结果表明：金属表面盐分的沉积显著加速了金属材质的停用腐蚀，采用充氮法排除定子内的氧气能够有效抑制金属腐蚀的发生；充氮保养系统投运后41 h，氮气纯度可达到98.8%，投运113 h后，定子内相对湿度降至5%以下，并长期保持稳定；试验过程中，发电机定子相关金属材质防腐效果良好，发电子定子绝缘电阻质量得到改善。

Abstract

The corrosion behavior of generator stator metal material in simulated high humidity salt spray environment was studied

and a nitrogen-charging maintenance system for generator stator was developed

and industrial tests were carried out on a 100 megawatt unit. The results show that

the deposition of salt on the metal surface accelerated the corrosion of the metal material

and the removal of oxygen from the stator by nitrogen filling method can effectively inhibit the corrosion of the metal material. The nitrogen purity reached 98.8% after 41 h of nitrogen charging and the maintenance system was put into operation

and the relative humidity in the stator decreased to below 5% after the system ran for 113 h. During the test

the anti-corrosion effect of the related metal materials of the generator stator was good

and the disqualification of the insulation resistance of the generator stator was effectively improved.

关键词

Keywords

references

浏览量

下载量

CSCD

文章被引用时，请邮件提醒。

提交

关联资源

珞璜电厂湿式石灰石-石膏法脱硫系统运行中存在的问题及其分析

锅炉进汽包口炉内加药管腐蚀原因分析

云浮电厂凝汽器铜管腐蚀穿孔原因分析及防护措施

300MW机组锅炉再热器和水冷壁频繁爆漏原因分析及其对策

锅炉“四管”爆漏原因分析